Regitex MG series


REGITEX MG Series is natural rubber latex which has been modified by graft polymerization of MMA  (Methyl Methacrylate). Depending on the grafting ratio, we have MG-10, MG-25, MG-40S and MG-67, which  demonstrate superior functions as the raw material for various adhesives and latex modifiers.


Application Examples
Base material for adhesives for leather shoes Used widely as the base material for heat resistant lasting adhesives and adhesives for uncured rubber tape


Base material of adhesives for textiles Utilized particularly where flexibility is demanded
PVC adhesive tape


Used in the base material for the primers to prevent  plasticizer migration, and in the adhesive layer
Adhesive for flocking


Has excellent adhesive properties with espect to cooking gloves, cured rubber for flocking glue and textiles
Modifier for dipped latex products By adding 5 to 10% to sulfur cured latex, hardness is increased and rubber degradation is effectively prevented
Modifiers of latex and emulsion based adhesives Effective in modifying the physical adhesive properties by adjusting the amount added to match the application
Base material for the adhesives for rubber particles for work gloves Rubber particles have high compound stability and excellent adhesion
Binder for leather board and pulp board Excellent as a binding agent on its own, and even as a base material for binding agents it has favorable compound stability
Binder for type chips Favorable as a coloring agent for tire chip surfaces
Base material for adhesives in paper processing Is used as the base material for cold sealing agents and reasonable adhesives
Base material for primers used principally for the p urpose of increasing the adhesion of rubber material Used by masticating and dissolving in organic solvent.



MG Series List

Latex Characteristics MG-10 MG-25 MG-40S MG-67

(B type, mPa.s)

30-100 20-80 20-80 20-100
pH 10+1 10+1 10+1 10+1
Total Solids


52+2 50+2 52+2 50+2


Physical Properties MG-10 MG-25 MG-40S MG-67
Modulus 100% (MPa) 0.6 1.1 1.8 2.3
Modulus 300% (MPa) 0.7 1.5 2.8 3.4
Modulus 600% (MPa) 1.8 5.8 9.9 11.7
Tensile Strength


16.5 30 23.5 24.5
Stretch (%) 1000 850 720 680


Conditions for fabrication of the test membrane:


  1. Film casting on glass
  2. Drying (room temperature, 1 day)

3. Heat treatment (90℃)